All our special products
-
TYPE: CLOTH ARAMID CARBON GLASS 650G WEIGHT: 650g/m² THICKNESS: 2mm CONSTRUCTION: WARP 78 ends per 10cm ARAMID/ CARBON BLEND with E-GLASS CORE TEX 260x2 WEFT 42 ends per 10cm ARAMID/ CARBON BLEND With E-GLASS CORE TEX 260x1 TENSILE STRENGTH WARP 1600 Newton per 5cm WEFT 1500 Newton per 5cm STANDARD WIDTH: 10500mm LENGTH OF ROLL: 50m OPERATING TEMPERATURE: 350° C depending on the application. Will withstand higher excursions temperatures and open flames for short periods of time. Suitable for high strength, high abrasion condition. Not suitable for UV light application. GENERAL A mixture of aramid, carbon and glass fibers which combine to provide high strength, high protection and high operating temperature. -
WEIGHT: 2100g/m² nominal THICKNESS: 3.0mm REINFORCEMENT: E-Glass Cloth/ 1000G OPERATING PRESSURE: 30kPa OPERATING TEMPERATURE: 145 °C dependent upon application GENERAL: Suitable for mild corrosion, and abrasive conditions. -
DESCRIPTION The Thermolastic Exhaust Insulation System was primarily designed for the purpose of maintaining gas temperatures in wide bore diesel exhausts fitted with a durable outer layer that is resistant to oil, water, UV and is easy to install. Thermolastic tape wrap insulation also lends itself to many other thermal application as the product combines an efficient high temperature insulation media with a durable outer layer that is resistant to oil, water, UV and is easy to install. CONSTRUCTION The system comprises two main components: an insulating layer of E- Glass tape and an outer protective tape layer. The inner layer consists of high temperature insulating E-Glass material bonded to a reflective film in a usable format that allows the tape to stretch thereby accommodating bends and avoiding slippage when wrapped. The protective outer layer is a grey, self bonding, high temperature resistant elastomer that provides extra protection to the reflective material and provides excellent resistance to UV and oxidation. The tape bonds readily to itself to provide a water and oil resistant coating while remaining durable enough to withstand the rigorous conditions found under-body on commercial vehicles. The tape is also fire retardant to UL 94 VO. The protective layer consists of an extruded self amalgamating silicone elastomer in roll form with a film interleave. It has a maximum continuous working temperature of 200°C with a spike temperature of 250°C. APPLICATION The Thermolastic wrap is applied in layers according to the temperatures involved normally 3 layers. For higher temperatures it is recommended that at least one plain insulation layer (knitted E- Glass without reflective film) is applied against the hot face with the reflective layers applied later. -
Description Volcano Wrap is made from continuous filament basalt fiber that resists gasoline and engine chemicals and withstands temperatures up to 650◦C. When wrapped around exhaust pipes, the unique construction creates an attractive and durable finished product. It is very rugged and will not exhibit any vibration damage over long periods of use. -
COMPOSITION: Mineral Fibres and Fillers THICKNESS: 3mm- 12mm STANDARD SIZE: 1000mm x1000mm COLOUR: Grey MAX OPERATING TEMPERATURE: 1000°C HEAT TREATMENT LOSS AT 800°C: 16% THERMAL (400°C) CONDUCTIVITY: 0.16W/m°K DENSITY: 1.0 COMPRESSIBILITY: 10% for 70kg/cm³ RECOVERY: 40% -
THERMOSHIELD 1635G CONTINUOUS OPERATING TEMPERATURE: 320°C EXCURSION TEMPERATURE: 350°C MAXIMUM PRESSURE: +/- 35kPa (5psi) THICKNESS: 1.4mm MASS: 1635g/m² CHEMICAL RESISTANCE: Sulphuric acid (Hot 50% solution)- little or no effect Hydrochloric acid (Hot 20% solution)- little or no effect Anhydrous ammonia - little or no effect Caustic soda (+20% solution) - little or no effect PERMEATION: None from either side especially when exposed to weather and harsh industrial condition. APPLICATIONS: Used in high-acid and harsh industrial conditions.